ASTM A1008 HSLAS Grade 310 Class 1
Equivalent material: DIN 1.0489, DIN ZStE 300, DIN H280LA, DIN HC300LA, AFNOR HC300LA, BS HC300LA, JIS SPFC440, EN HC300LA, EN H280LA, EN 1.0489, ISO 300Y, GB/T CR300LA, ASTM HSLAS Grade 310 Class 2, DIN 1.0548, DIN H320LA, DIN ZStE 340, DIN HC340LA, AFNOR HC340LA, AFNOR E315C, AFNOR H315M, AFNOR H320M, BS HC340LA, JIS SPFC490, EN HC340LA, EN H320LA, EN 1.0548, ISO 340Y, GB/T CR340LA, ASTM HSLAS Grade 340 Class 1, ASTM HSLAS Grade 340 Class 2
ASTM A1008 HSLAS Grade 310 Class 1 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS Grade 310 Class 1 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS Grade 310 Class 1 chemical
| Property |
Value |
| Carbon |
Carbon of 0.22 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 1.65 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 5E-3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.04 % |
| Titanium |
Titanium of 5E-3 % |
| Vanadium |
Vanadium of 5E-3 % |
ASTM A1008 HSLAS Grade 310 Class 1 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS Grade 310 Class 1 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1008 HSLAS Grade 310 Class 1 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 410 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 310 MPa |
- |