ASTM A1008 HSLAS-F Grade 480
Equivalent material: DIN 1.0984, DIN QStE 500 TM, DIN S500MC, AFNOR S500MC, AFNOR S490MC, AFNOR E490D, BS S500MC, EN S500MC, EN 1.0984, ISO HSF490, ISO FeE500, ISO FeE490, ASTM HSLAS Grade 480 Class 1, ASTM HSLAS Grade 480 Class 2
ASTM A1008 HSLAS-F Grade 480 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS-F Grade 480 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS-F Grade 480 chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 1.65 % |
| Molybdenum |
Molybdenum of 0.16 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 5E-3 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Sulfur |
Sulfur of 0.025 % |
| Titanium |
Titanium of 5E-3 % |
| Vanadium |
Vanadium of 5E-3 % |
ASTM A1008 HSLAS-F Grade 480 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1008 HSLAS-F Grade 480 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1008 HSLAS-F Grade 480 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 16 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 550 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 480 MPa |
- |