AISI 422 Heat Treated
Equivalent material: DIN 1.4929, DIN X23CrMoWMnNiV12-1-1, SAE 422, JIS SUH616, EN 1.4929, ISO X23CrMoWMnNiV12-1-1, ISO 4929-422-00-I, ISO MM13J, GB/T 22Cr12NiWMoV, GB/T 47220, GB/T 2Cr12NiMo1W1V, GB/T S47520, ASTM B4B, ASTM B4C, UNS S42200, DIN 1.4935, DIN X20CrMoWV12-1, AFNOR X20CrMoWV12-1, BS X20CrMoWV12-1, AISI HNV-8, SAE HNV-8, EN X20CrMoWV12-1, EN 1.4935, GOST 15Ch12WNMF, GB/T S47220, AMS 5655, ASTM Grade 616
AISI 422 Heat Treated general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 422 Heat Treated thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
| Melting point |
- |
Melting point of 1470 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 24 W/(m·K) |
AISI 422 Heat Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.2 - 0.25 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Iron |
Iron of 81.9 - 85.8 % |
| Manganese |
Manganese of 0.5 - 1 % |
| Molybdenum |
Molybdenum of 0.9 - 1.3 % |
| Nickel |
Nickel of 0.5 - 1 % |
| Phosphorus |
Phosphorus of 0 - 0.03 % |
| Silicon |
Silicon of 0 - 0.5 % |
| Sulfur |
Sulfur of 0 - 0.025 % |
| Tungsten |
Tungsten of 0.9 - 1.3 % |
| Vanadium |
Vanadium of 0.2 - 0.3 % |
AISI 422 Heat Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
AISI 422 Heat Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1110 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 870 MPa |
- |