JIS G4311 Grade SUH616 quenched and tempered
Equivalent material: GB/T 2Cr12NiMoWV, ASTM S42100, AISI S42100, GOST 15Х12ВНМФ, GOST 15H12VNMF, GOST 15H12VNMF-Sh, BS 762, UNI X22CrMoWV121, AMS 5655, ASTM 616, MIL 422, AISI 422, SAE 422, SAE HNV-8, DIN 1.4935, DIN X20CrMoWV12-1, AFNOR X20CrMoWV12-1, BS X20CrMoWV12-1, AISI HNV-8, EN X20CrMoWV12-1, EN 1.4935, GOST 15Ch12WNMF, GB/T 22Cr12NiWMoV, GB/T S47220, ASTM Grade 616, ASTM B4B, ASTM B4C, UNS S42200, DIN 1.4929, DIN X23CrMoWMnNiV12-1-1, EN 1.4929, ISO X23CrMoWMnNiV12-1-1, ISO 4929-422-00-I, ISO MM13J, GB/T 47220, GB/T 2Cr12NiMo1W1V, GB/T S47520
JIS G4311 Grade SUH616 quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4311 Grade SUH616 quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4311 Grade SUH616 quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4311 Grade SUH616 quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 10 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 341 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 25 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 880 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 735 MPa |
- |