AISI 321 Hot Finished
Equivalent material: DIN 1.4541, DIN X6CrNiTi18-10, DIN X10CrNiMoTi18-10, AFNOR Z6CNT18-10, BS 321S12, BS 321S51, UNI X6CrNiTi1811, SS 2337, UNE F.3553, UNE F.3523, SAE 321, JIS SUS321, JIS SUS321TPY, JIS SUS321TP, JIS SUS321TF, JIS SUS321TB, EN X6CrNiTi18-10, EN 1.4541, GOST 06Ch18N10T, GOST 08X18H10T, GOST 12X18H10T, GB 0Cr18Ni11Ti, UNS S32100, IS X04Cr18Ni10Ti, JIS SUSF321, ASTM TP321, ASTM 321, ASTM Grade F321, ASTM F321, ASTM Grade 8T, ASTM S32100, ASTM FP321, ASTM MT321, ASTM Grade B8T, ASTM Grade B8TA, ASTM Grade 8TA, ASTM Grade 8T, DIN 1.4544, DIN 1.4544.9, AFNOR 9160/C 63, AFNOR 9160C201, AFNOR Z 10 CNT 18-11, BS S524, BS S526, BS 2 S129, AISI S32100, SAE S32100, EN FE-PA 13, EN 1.4544, GOST 08Ch18N12T
AISI 321 Hot Finished general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 321 Hot Finished thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 16 W/(m·K) |
AISI 321 Hot Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.08 % |
| Chromium |
Chromium of 17 - 19 % |
| Iron |
Iron of 65.2 - 74 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 9 - 12 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
| Titanium |
Titanium of 0 - 0.7 % |
AISI 321 Hot Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 321 Hot Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 51 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 230 MPa |
- |
Collaborate with us to explore innovative possibilities using our cutting-edge steel technologies.