AISI 316LN Solution Treated
Equivalent material: DIN 1.4406, DIN X2CrNiMoN17-11-2, AFNOR Z3CND17-11Az, BS 316S61, BS 316S13, UNE F.3542, SAE 316LN, JIS SUS316LN, EN X2CrNiMoN17-11-2, EN 1.4406, UNS S31653, DIN 1.4429, DIN X2CrNiMoN17-13-3, AFNOR Z7CND18-12-03, BS 316S63, UNI X2CrNiMoN1713, SS 2375, JIS SUSF316LN, EN X2CrNiMoN17-13-3, EN 1.4429, ASTM S31654, UNS S31654, DIN 1.4910, DIN X3CrNiMoN17-13, DIN X3CrNiMoBN17-13-3, EN X3CrNiMoBN17-13-3, EN X3CrNiMoN17-13-3, EN X3CrNiMoNB17-13-3, EN X3NiMoN17-13-3, EN 1.4910, ASTM S31653, ASTM TP316LN, ASTM 316LN, ASTM F316LN, ASTM Grade 8MLN
AISI 316LN Solution Treated general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 316LN Solution Treated thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1380 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 480 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 316LN Solution Treated chemical
| Property |
Value |
| Boron |
Boron of 1.5E-3 - 5E-3 % |
| Carbon |
Carbon of 0 - 0.04 % |
| Chromium |
Chromium of 16 - 18.5 % |
| Iron |
Iron of 61.2 - 71.9 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 10 - 14 % |
| Nitrogen |
Nitrogen of 0.1 - 0.22 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 316LN Solution Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 316LN Solution Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 40 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 680 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 320 MPa |
- |