AISI 304L Quarter-Hard
Equivalent material: DIN 1.4306, DIN X2CrNi19-11, DIN 19Cr11Ni, AFNOR Z3CN18-10, BS 304S11, SS 2352, SAE 304L, JIS SUS304L, JIS SCS19, JIS SCS19A, JIS SUS304LTB, JIS SUS304LTP, JIS SUS304LTPY, JIS SUS304LTBS, JIS SUSF304L, EN X2CrNi19-11, EN 1.4306, ISO A3, GB 00Cr19Ni10, ASTM Grade CPF3, UNS S30403, DIN 1.4307, DIN G-X2CrNiN18-9, AFNOR Z3CN19-09, EN X2CrNi18-9, EN 1.4307, GOST 03Ch18N11, ASTM TP304L, IS X02Cr18Ni11, DIN 1.4309, BS 304C12, JIS SCS13, EN GX2CrNi19-11, EN 1.4309, ASTM CF3, UNS J92500, ASTM 304L, ASTM S30403, ASTM F304L, ASTM MT304L
AISI 304L Quarter-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 304L Quarter-Hard thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 16 W/(m·K) |
AISI 304L Quarter-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.03 % |
| Chromium |
Chromium of 17.5 - 20 % |
| Iron |
Iron of 64.8 - 74.5 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 8 - 12 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 304L Quarter-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 304L Quarter-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 990 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 590 MPa |
- |
Create sustainable legacies with our eco-friendly steel materials and practices.
-- Our promise
Similar or equivalent steel materials