AISI 304 Half-Hard
Equivalent material: DIN 1.4301, DIN X 5 CrNi 18 9, DIN X5CrNi18-10, AFNOR Z6CN18-09, AFNOR Z7CN18-09, BS 304S15, BS 304S31, UNI X5CrNi1810, SS 2332, UNE F.3551, SAE 304, JIS SUS304, JIS SUS304TBS, JIS SUS304TPD, JIS SUS304TP, JIS SUS304TPY, JIS SUS304TB, JIS SUS304TF, JIS SUS304TKA, JIS SUS304TKC, JIS SUSF304, EN X5CrNi18-10, EN 1.4301, ISO A2, GOST 08Ch18N10, GB 0Cr18Ni9, ASTM TP304, ASTM Grade B8, ASTM Grade B8A, ASTM 304, UNS S30400, DIN 1.4350, DIN X5CrNi18-9, AFNOR Z6CN18.09, SS 2333, EN 1.4350, ASTM S30400, ASTM Grade F304, ASTM F304, ASTM Grade 8, ASTM FP304, ASTM MT304, ASTM Grade 8A, DIN 1.4314, AFNOR 9160/C 109, AFNOR 9160C411, AFNOR Z 12 CN 18-10, AISI 305, SAE 305, EN FE-PA 11, EN FE-PA 12, EN 1.4314, ASTM 305
AISI 304 Half-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 304 Half-Hard thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 16 W/(m·K) |
AISI 304 Half-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.08 % |
| Chromium |
Chromium of 17.5 - 20 % |
| Iron |
Iron of 66.5 - 74.5 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 8 - 10.5 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 304 Half-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 304 Half-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 8.1 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1190 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 870 MPa |
- |