AISI 205 Quarter-Hard
Equivalent material: SAE 205, ASTM 205, UNS S20500
AISI 205 Quarter-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.6 g/cm³ |
AISI 205 Quarter-Hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
AISI 205 Quarter-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.25 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Iron |
Iron of 62.6 - 68.1 % |
| Manganese |
Manganese of 14 - 15.5 % |
| Nickel |
Nickel of 1 - 1.7 % |
| Nitrogen |
Nitrogen of 0.32 - 0.4 % |
| Phosphorus |
Phosphorus of 0 - 0.06 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 205 Quarter-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 205 Quarter-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 52 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 990 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 590 MPa |
- |