ASTM A666 Grade 205 1/8 Hard
Equivalent material: AISI 205, SAE 205, UNS S20500
ASTM A666 Grade 205 1/8 Hard general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A666 Grade 205 1/8 Hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A666 Grade 205 1/8 Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.25 % |
| Chromium |
Chromium of 16.5 - 18 % |
| Manganese |
Manganese of 14 - 15 % |
| Nickel |
Nickel of 1 - 1.75 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.75 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A666 Grade 205 1/8 Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A666 Grade 205 1/8 Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 40 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 450 MPa |
- |
Choose our long-lasting steel products for enduring performance and reliability.