AISI 1527 Hot Rolled
Equivalent material: DIN 1.1170, DIN 28Mn6, DIN ETG 25, AFNOR 28Mn6, AFNOR 20M5, BS 26Mn6, BS En14A, BS En14B, BS 150M19, AISI 1330H, AISI 1330, AISI 1524, SAE 1330H, SAE 1527, SAE 1330, SAE 1524, JIS S33C, JIS SCMn1A, JIS SCMn1B, JIS SCMn1, EN 28Mn6, EN 1.1170, ISO 28Mn6, GOST 30G2, GB 30Mn2, GB A00302, GB/T 30Mn2, GB/T A00302, UNS H13300, UNS G13300, IS 20Mn2, IS 20C15, DIN 1.1161, DIN 26Mn5, AFNOR 26Mn5, BS 26Mn5, AISI 1526, SAE 1526, EN 26Mn5, EN 1.1161, ASTM 1526, UNS G15260, UNS G15270
AISI 1527 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1527 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
AISI 1527 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.22 - 0.29 % |
| Iron |
Iron of 98.1 - 98.6 % |
| Manganese |
Manganese of 1.2 - 1.5 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1527 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 600 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 330 MPa |
- |