AISI 1080 Spheroidized And Cold Drawn
Equivalent material: DIN 1.1265, DIN D85-3, DIN C86D2, AFNOR C86D2, BS C86D2, SAE 1080, EN C86D2, EN 1.1265, ISO C86D2, GB/T C86D2, ASTM 1080, UNS G10800, DIN 1.0616, DIN D 85-2, DIN C86D, AFNOR C86D, BS C86D, BS 80CS, BS 80HS, AISI 1086, SAE 1086, JIS CS85, EN C86D, EN 1.0616, ISO C86D, ISO CS85, GOST 85, GB 85, GB U53862, GB U20852, GB/T C86D, GB/T U53862, GB/T 85, GB/T U20852, GB/T U59863, UNS G10860
AISI 1080 Spheroidized And Cold Drawn general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1080 Spheroidized And Cold Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1080 Spheroidized And Cold Drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.75 - 0.88 % |
| Iron |
Iron of 98.1 - 98.7 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1080 Spheroidized And Cold Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1080 Spheroidized And Cold Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 780 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 590 MPa |
- |