AISI 1080 Hot Rolled

Equivalent material: DIN 1.1265, DIN D85-3, DIN C86D2, AFNOR C86D2, BS C86D2, SAE 1080, EN C86D2, EN 1.1265, ISO C86D2, GB/T C86D2, ASTM 1080, UNS G10800, DIN 1.0616, DIN D 85-2, DIN C86D, AFNOR C86D, BS C86D, BS 80CS, BS 80HS, AISI 1086, SAE 1086, JIS CS85, EN C86D, EN 1.0616, ISO C86D, ISO CS85, GOST 85, GB 85, GB U53862, GB U20852, GB/T C86D, GB/T U53862, GB/T 85, GB/T U20852, GB/T U59863, UNS G10860

AISI 1080 Hot Rolled general

Property Temperature Value
Density 23.0 °C Density of 7.8 g/cm³

AISI 1080 Hot Rolled thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1289 - 1478 °C Typical for High Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 450 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 36 W/(m·K) Typical for High Carbon Steel

AISI 1080 Hot Rolled chemical

Property Value
Carbon Carbon of 0.75 - 0.88 %
Iron Iron of 98.1 - 98.7 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0 - 0.04 %
Sulfur Sulfur of 0 - 0.05 %

AISI 1080 Hot Rolled electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

AISI 1080 Hot Rolled mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 12 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for High Carbon Steel
Shear modulus 23.0 °C Shear modulus of 81 GPa Typical for High Carbon Steel
Tensile strength 23.0 °C Tensile strength of 890 MPa -
Yield strength 23.0 °C Yield strength of 490 MPa -