AISI 1065 Hot Rolled
Equivalent material: DIN 1.0611, DIN D 63-2, DIN C62D, AFNOR C62D, BS C62D, SAE 1065, JIS SWRH62, JIS SWRH62A, JIS CS65, EN C62D, EN 1.0611, ISO C62D, GB C62D, GB U53622, GB/T C62D, GB/T U53622, GB/T U59622, UNS G10650, DIN 1.0612, DIN D 65-2, DIN C66D, AFNOR C66D, BS C66D, EN C66D, EN 1.0612, ISO C66D, ISO CS65, GOST 65, GB C66D, GB U59662, GB/T C66D, GB/T U53662, GB/T U59662, DIN 1.1230, DIN C65S1, BS 060A96, JIS SWO-V, EN 1.1230, GOST 65GA, GOST 68A, GB/T 65, GB/T U20652, ASTM 1065, IS 65C6, DIN 1.0613, DIN D 68-2, DIN C68D, AFNOR C68D, BS C68D, AISI 1064, SAE 1064, JIS SWRH67, JIS CS70, EN C68D, EN 1.0613, ISO C68D, GB C68D, GB U59682, GB/T C68D, GB/T U53682, GB/T U59682, UNS G10640
AISI 1065 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1065 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1065 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.6 - 0.7 % |
| Iron |
Iron of 98.3 - 98.8 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1065 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1065 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 14 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |