AISI 1055 Hot Rolled
Equivalent material: DIN 1.0535, DIN C55, AFNOR C54, AFNOR C55, AFNOR AF70, BS 070M55, BS En9, BS En43A, BS C55, BS 080M50, UNI C55, SS 1655, SAE 1055, JIS S55C, JIS S55CM, EN C55, EN 1.0535, ISO C55, ISO CS55, GOST 55, GB/T 55, GB/T U20552, ASTM 1055, UNS G10550, IS 55C8, IS C55Mn75, DIN 1.1203, DIN Ck55, DIN C55E, AFNOR XC55, AFNOR XC54, AFNOR XC50, AFNOR C55RR, AFNOR C55E, AFNOR XC55H1, BS C55E, UNI C50, UNE C55K, JIS S55C-CSP, EN C55E, EN 1.1203, ISO C55E, ISO C55E4, ISO S55C, GB 55, GB U20552, GB/T ZG55, GB/T C23464, GB/T ZG340-640, GB/T SM55, GB/T T10550, DIN 1.1209, DIN Cm55, DIN C55R, DIN C55S, AFNOR C55R, AFNOR XC55H1u, BS C55R, EN C55R, EN C55S, EN 1.1209, ISO C55M2, ISO C55R, DIN 1.1220, DIN D 55-3, DIN C56D2, AFNOR C56D2, BS C56D2, EN C56D2, EN 1.1220, ISO C56D2, GB/T C56D2, DIN 1.1213, DIN C53G, DIN Cf 53, DIN C53E, DIN Cf53, AFNOR XC48TS, UNI C53, SS 1674, AISI 1050, SAE 1050, JIS S50C, JIS S50CM, EN C53G, EN 1.1213, ISO S50C, UNS G10500, IS 55C6
AISI 1055 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1055 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
AISI 1055 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.5 - 0.6 % |
| Iron |
Iron of 98.4 - 98.9 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1055 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1055 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 14 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 750 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 410 MPa |
- |
Have confidence in the strength and durability of our steel materials.