IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered
Equivalent material: 55C8, DIN 1.0535, DIN C55, AFNOR C54, AFNOR C55, AFNOR AF70, BS 070M55, BS En9, BS En43A, BS C55, BS 080M50, UNI C55, SS 1655, AISI 1055, SAE 1055, JIS S55C, JIS S55CM, EN C55, EN 1.0535, ISO C55, ISO CS55, GOST 55, GB/T 55, GB/T U20552, ASTM 1055, UNS G10550, IS 55C8, DIN 1.1203, DIN Ck55, DIN C55E, AFNOR XC55, AFNOR XC54, AFNOR XC50, AFNOR C55RR, AFNOR C55E, AFNOR XC55H1, BS C55E, UNI C50, UNE C55K, JIS S55C-CSP, EN C55E, EN 1.1203, ISO C55E, ISO C55E4, ISO S55C, GB 55, GB U20552, GB/T ZG55, GB/T C23464, GB/T ZG340-640, GB/T SM55, GB/T T10550
IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.85 g/cm³ |
IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for Medium Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 470 - 520 J/(kg·K) |
Typical for Medium Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.5 - 0.6 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
IS 1570 Grade C55Mn75 Hot Rolled/Normalized/Cold Drawn/Hardened-Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
In Normalized Condition |
| Elongation |
23.0 °C |
Elongation of 7 - 18 % |
For Different Conditions |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 197 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 92 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.27 [-] |
In Normalized Condition |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 630 - 950 MPa |
For Different Conditions |
| Yield strength |
23.0 °C |
Yield strength of 560 MPa |
- |