AISI 1049 Hot Rolled
Equivalent material: DIN 1.1171, DIN C50D2, AFNOR C50D2, BS C50D2, SAE 1049, EN C50D2, EN 1.1171, ISO C50D2, GB/T SM50, GB/T T10500, GB/T C50D2, UNS G10490, DIN 1.0540, DIN C50, AFNOR C50, BS C50, BS 50HS, BS 50CS, AISI 1050, SAE 1050, JIS S53, JIS S50, JIS STKM17A, JIS 17C, JIS 17A, JIS STKM17C, JIS CS50, EN C50, EN 1.0540, ISO C50, ISO CS50, GOST 50, ASTM Grade 1050, UNS G10500, DIN 1.1201, DIN Cm 45, DIN Cm45, DIN C45R, AFNOR C45R, AFNOR XC48H1u, BS C45R, AISI 1045, SAE 1045, EN C45R, EN 1.1201, ISO C45R, ISO C45M2, UNS G10450, DIN 1.1206, DIN Ck50, DIN C50E, AFNOR C50E, AFNOR XC50, BS En43A, BS C50E, BS 080M50, BS CS50, JIS S50C, JIS S53C, EN C50E, EN 1.1206, ISO C50E, ISO C50E4, GB SM50, GB T10500, GB/T 50, GB/T U20502
AISI 1049 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1049 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
AISI 1049 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.46 - 0.53 % |
| Iron |
Iron of 98.5 - 98.9 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1049 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1049 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 17 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 690 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 380 MPa |
- |
Our quality control measures guarantee the highest standards of steel.
-- Our promise