AISI 1042 Hot Rolled

AISI 1042 Hot Rolled

Equivalent material: DIN 1.1162, DIN C46D2, AFNOR C46D2, BS C46D2, SAE 1042, EN C46D2, EN 1.1162, ISO C46D2, GB/T C46D2, ASTM 1042, UNS G10420, DIN 1.0541, DIN D 40-2, DIN C42D, AFNOR C42D, BS C42D, AISI 1043, SAE 1043, JIS SWRH42, JIS SWRH42A, EN C42D, EN 1.0541, ISO C42D, GOST 45, GB 45, GB U20452, ASTM 1043, UNS G10430, DIN 1.1154, DIN C42D2, AFNOR C42D2, BS C42D2, JIS S43C, EN C42D2, EN 1.1154, ISO C42D2, GB C42D2, GB/T C42D2

AISI 1042 Hot Rolled general

Property Temperature Value
Density 23.0 °C Density of 7.8 g/cm³

AISI 1042 Hot Rolled thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1380 - 1514 °C Typical for Medium Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 450 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 21 - 52 W/(m·K) Typical for Medium Carbon Steel

AISI 1042 Hot Rolled chemical

Property Value
Carbon Carbon of 0.4 - 0.47 %
Iron Iron of 98.5 - 99 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0 - 0.04 %
Sulfur Sulfur of 0 - 0.05 %

AISI 1042 Hot Rolled electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

AISI 1042 Hot Rolled mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 18 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Medium Carbon Steel
Shear modulus 23.0 °C Shear modulus of 75 - 80 GPa Typical for Carbon Steel
Tensile strength 23.0 °C Tensile strength of 630 MPa -
Yield strength 23.0 °C Yield strength of 350 MPa -