AISI 1018 Cold Drawn

Equivalent material: DIN 1.0419, DIN RSt44-2, DIN RSt 44-2, AFNOR 14-13-12E, BS 43A, SAE 1018, JIS SWRCH18A, JIS SWRCH18K, JIS SWRCH16A, JIS SWRCH16K, JIS SWRCH19A, EN S275, EN 1.0419, GOST St 3-sp, GOST St3sp, GB ML3, ASTM 1018, ASTM Grade 1018, UNS G10180, IS 15C8

AISI 1018 Cold Drawn general

Property Temperature Value
Density 23.0 °C Density of 7.9 g/cm³

AISI 1018 Cold Drawn thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 450 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

AISI 1018 Cold Drawn chemical

Property Value
Carbon Carbon of 0.15 - 0.2 %
Iron Iron of 98.8 - 99.25 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0 - 0.04 %
Sulfur Sulfur of 0 - 0.05 %

AISI 1018 Cold Drawn magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

AISI 1018 Cold Drawn electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

AISI 1018 Cold Drawn mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 16 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 23.0 °C Tensile strength of 470 MPa -
Yield strength 23.0 °C Yield strength of 400 MPa -