AISI 1016 Hot Rolled
Equivalent material: DIN 1.0407, DIN C16, AFNOR C16, BS 080A15, BS EN32B, BS C16, SS 1370, SAE 1016, EN C16, EN 1.0407, ASTM Grade 1016, UNS G10160, DIN 1.1148, DIN Ck15Al, DIN C16E, AFNOR C16E, BS C16E, BS En32C, BS S14, BS 4S14, BS 080M15, EN C16E, EN 1.1148, ISO C16E, ISO C16E4, GB/T 15AI, GB/T U22152, DIN 1.1208, DIN C16R, AFNOR C16R, BS C16R, EN C16R, EN 1.1208, ISO C16R, ISO C16M2, DIN 1.0401, DIN St 37-2, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, UNI C15C16, SS 1350, UNE F.111, AISI 1015, AISI 1017, SAE 1015, SAE 1017, JIS S15C, EN C15, EN 1.0401, ASTM M1015, ASTM Grade 1015, UNS G10150, UNS G10170
AISI 1016 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1016 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1016 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.13 - 0.18 % |
| Iron |
Iron of 98.8 - 99.27 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1016 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1016 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1016 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 29 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 440 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 240 MPa |
- |