AISI 1015 Hot Rolled
Equivalent material: DIN 1.0413, DIN D 15-2, DIN C15D, AFNOR C15D, BS C15D, SAE 1015, JIS SWRM15, EN C15D, EN 1.0413, ISO C15D, UNS G10150, DIN 1.1132, DIN Cq15, DIN C15E2C, AFNOR FR15, AFNOR C15E2C, BS C15E2C, JIS SWRCH15K, JIS SWCH15K, EN C15E2C, EN 1.1132, GB/T ML18, GB/T U40182, GB/T ML15, GB/T U40152, ASTM M1015, DIN 1.1140, DIN Cm15, DIN C15R, AFNOR C15R, EN C15R, EN 1.1140, ISO C15R, ISO C15M2, ASTM Grade 1015, DIN 1.0401, DIN St 37-2, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, BS 080M15, UNI C15C16, SS 1350, UNE F.111, AISI 1017, AISI 1016, SAE 1017, SAE 1016, JIS S15C, EN C15, EN 1.0401, UNS G10170, DIN 1.1141, DIN Ck15, DIN C15E, AFNOR C15E, AFNOR XC18, AFNOR C18RR, AFNOR XC15, BS C15E, BS En32C, BS 080A15, UNI C16, SS 1370, UNE C15K, JIS S15CK, EN C15E, EN 1.1141, ISO C15E4, ISO C15E, ISO S15C, GOST 15, GB/T 15, GB/T U20152
AISI 1015 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 1015 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
AISI 1015 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.13 - 0.18 % |
| Iron |
Iron of 99.13 - 99.57 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1015 Hot Rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
AISI 1015 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1015 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 32 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 390 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 220 MPa |
- |