UNS S35500 Hardened
Equivalent material: ASTM 634
UNS S35500 Hardened general
| Property | Temperature | Value |
|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ |
UNS S35500 Hardened thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.3E-5 1/K | - |
| Melting point | - | Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 450 J/(kg·K) | - |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
UNS S35500 Hardened chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.1 - 0.15 % |
| Chromium | Chromium of 15 - 16 % |
| Iron | Iron of 73.2 - 77.7 % |
| Manganese | Manganese of 0.5 - 1.3 % |
| Molybdenum | Molybdenum of 2.5 - 3.2 % |
| Nickel | Nickel of 4 - 5 % |
| Niobium | Niobium of 0.1 - 0.5 % |
| Nitrogen | Nitrogen of 0.07 - 0.13 % |
| Phosphorus | Phosphorus of 0 - 0.04 % |
| Silicon | Silicon of 0 - 0.5 % |
| Sulfur | Sulfur of 0 - 0.03 % |
UNS S35500 Hardened electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
UNS S35500 Hardened mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 220 GPa | - |
| Elongation | 23.0 °C | Elongation of 14 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 1350 - 1510 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 1230 - 1310 MPa | - |