UNS S34565 Annealed
Equivalent material: DIN 1.4565, DIN X2CrNiMnMoNbN25-18-5-4, AISI S34565, SAE S34565, EN X3CrNiMnMoNbN23-17-5-3, EN 1.4565, ASTM S34565, ASTM F49
UNS S34565 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
UNS S34565 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 12 W/(m·K) |
- |
UNS S34565 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.03 % |
| Chromium |
Chromium of 23 - 26 % |
| Iron |
Iron of 41.2 - 51.6 % |
| Manganese |
Manganese of 5 - 7 % |
| Molybdenum |
Molybdenum of 4 - 5 % |
| Nickel |
Nickel of 16 - 19 % |
| Niobium |
Niobium of 0 - 0.15 % |
| Nitrogen |
Nitrogen of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.03 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.015 % |
UNS S34565 Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
UNS S34565 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 40 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 910 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 480 MPa |
- |