UNS S32750 Annealed
Equivalent material: DIN 1.4410, DIN GX10CrNiMo18-9, AFNOR Z3CND25-06Az, AISI A182 F53, AISI S32750, SAE A182 F53, SAE S32750, EN X2CrNiMoN25-7-4, EN 1.4410, GB 022Cr25Ni7Mo4N, ASTM Type 2507, ASTM F53, ASTM S32750, ASTM 2507
UNS S32750 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
UNS S32750 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
UNS S32750 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.03 % |
| Chromium |
Chromium of 24 - 26 % |
| Copper |
Copper of 0 - 0.5 % |
| Iron |
Iron of 58.1 - 66.8 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 3 - 5 % |
| Nickel |
Nickel of 6 - 8 % |
| Nitrogen |
Nitrogen of 0.24 - 0.35 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.02 % |
UNS S32750 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 17 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 890 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 610 MPa |
- |