UNS S30600 Solution Treated
Equivalent material: DIN 1.4361, AFNOR Z1CNS17-15, EN X1CrNiSi18-15-4, EN 1.4361, ASTM S30600, AISI S30600, SAE S30600, ASTM F46
UNS S30600 Solution Treated general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.7 g/cm³ |
UNS S30600 Solution Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 W/(m·K) |
- |
UNS S30600 Solution Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.018 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Copper |
Copper of 0 - 0.5 % |
| Iron |
Iron of 58.7 - 65.8 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 0 - 0.2 % |
| Nickel |
Nickel of 14 - 16 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.03 % |
| Silicon |
Silicon of 3.7 - 4.5 % |
| Sulfur |
Sulfur of 0 - 0.02 % |
UNS S30600 Solution Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
UNS S30600 Solution Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 46 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 630 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 250 MPa |
- |