UGIMA® 4571 Work Hardened (drawn)
UGIMA® 4571 Work Hardened (drawn) introduction
UGIMA® 4571 is an improved machinability stainless steel manufactured only by Ugitech.
Its properties are identical to those of 4571 except for its machinability, which is even better than that of 4571:
UGIMA® 4571's new technological advances are extremely advantageous, whatever the machining conditions, machine or tooling used.
Productivity increases of 15 to 30% over grade 4571, the current market standard, have been obtained.
Non-magnetic in annealed condition.
Slight magnetism is produced by cold-working operations
Equivalent material: DIN 1.4571, DIN X6CrNiMoTi17-12-2, EN 1.4571, EN X6CrNiMoTi17-12-2, JIS SUS316 Ti, ISO 4571-316-35-I, ISO X6CrNiMoTi17-12-2, AFNOR Z6CNDT17.12, BS 320S31, SS 2350
UGIMA® 4571 Work Hardened (drawn) general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGIMA® 4571 Work Hardened (drawn) thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.0000168 1/K |
20 to 200°C |
| Thermal conductivity |
Thermal conductivity of 15 W/(m·K) |
- |
UGIMA® 4571 Work Hardened (drawn) chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.05 |
max. |
| Chromium |
Chromium of 16.5 - 18.5 % |
- |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 2.0 - 2.5 % |
- |
| Nickel |
Nickel of 10.5 - 11.5 % |
- |
| Phosphorus |
Phosphorus of 0.045 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.015 - 0.03 % |
- |
| Titanium |
Titanium of 0.7000000000000001 |
max., min: 5xC |
UGIMA® 4571 Work Hardened (drawn) electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.4e-07 Ω·m |
UGIMA® 4571 Work Hardened (drawn) mechanical
| Property |
Value |
| Elastic modulus |
Elastic modulus of 200 GPa |
| Elongation |
Elongation of 31.0 - 52.0 % |
| Reduction of area |
Reduction of area of 66.0 - 70.0 % |
| Tensile strength |
Tensile strength of 620.0 - 760.0 MPa |
UGIMA® 4571 Work Hardened (drawn) application
| Property |
- |
- |
| Corrosion properties |
Environment |
Behavior |
| Nitric acid |
Good |
| Phosphoric acid |
Average |
| Sulphuric acid |
Average |
| Acetic acid |
Good |
| Sodium carbonate |
Average |
| NaCl (Saline mist) |
Good |
| Humidity |
Excellent |
| Petroleum |
Average |
| Sea water |
Average |