UGI 4404FGX3 Drawn Bar
UGI 4404FGX3 Drawn Bar introduction
UGI 4404FGX3 is a molybdenum austenitic stainless steel belonging to the 316L family. Its low carbon content provides good corrosion resistance on welded areas. In addition, UGI 4404FGX3 has good machinability properties.
UGI 4404FGX3 has a mainly austenitic microstructure with traces of residual ferrite (1 to 3%).
UGI 4404FGX3 is an austenitic grade and therefore practically non-magnetic after annealing treatment (relative permeability close to 1). Slight ferromagnetic behaviour can however be observed due to the presence of residual ferrite and/or strain-induced martensite after cold working the metal (for example after drawing).
Equivalent material: EN 1.4401, EN X5CrNiMo17-12-2, EN 1.4404, EN X2CrNiMo17-12-2, UNS S31600, UNS S31603, JIS SUS316, JIS SUS316L, ISO 4401-316-00-I, ISO X5CrNiMo17-12-2, ISO 4404-316-03-I, ISO X2CrNiMo17-12-2, AISI 316, AISI 316L, AFNOR Z7CND 17-11-02, AFNOR Z3CND 17-11-02, DIN 1.4401, DIN 1.4404, DIN X5CrNiMo17-12-2, DIN X2CrNiMo17-12-2, BS 316S11, BS 316S31, SS 2347, SS 2348
UGI 4404FGX3 Drawn Bar general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGI 4404FGX3 Drawn Bar thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.000016 1/K |
20 to 100°C |
| - |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 200°C |
| - |
Coefficient of thermal expansion of 0.000017 1/K |
20 to 300°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15 W/(m·K) |
- |
UGI 4404FGX3 Drawn Bar chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 16.5 - 18.5 % |
- |
| Copper |
Copper of 0.6000000000000001 |
max. |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 2.0 - 2.5 % |
- |
| Nickel |
Nickel of 11.0 - 13.0 % |
- |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.01 - 0.02 % |
- |
UGI 4404FGX3 Drawn Bar electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.5e-07 Ω·m |
UGI 4404FGX3 Drawn Bar mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy, V-notch |
- |
Charpy impact energy, V-notch of 100 J |
min. |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
- |
| - |
100 °C |
Elastic modulus of 194 GPa |
- |
| - |
200 °C |
Elastic modulus of 186 GPa |
- |
| - |
300 °C |
Elastic modulus of 179 GPa |
- |
| Elongation |
- |
Elongation of 30 % |
min. |
| Hardness, Brinell |
- |
Hardness, Brinell of 150.0 - 220.0 [-] |
- |
| Reduction of area |
- |
Reduction of area of 60.0 % |
min. |
| Tensile strength |
- |
Tensile strength of 550.0 - 800.0 MPa |
- |
UGI 4404FGX3 Drawn Bar application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
| General machinability |
| Heat Treatment |
| Hot forming |
| Other |
Product |
Shape |
Finishing |
Tolerance |
Dimensions (mm) |
| Rolled descaled |
k13 |
Ø 13 to 130 |
| Turned |
10+11 |
Ø 22 to 130 |
| Ground |
7+8+9+options |
Ø 2 to 130 |
| Drawn |
9 |
Ø 2 to 30 |
| Black bar |
+/- 1% of ø |
Ø 23 to 135 |
| Hexagonal |
Drawn |
10+11 |
Hex 3 to 55 |
| Rolled |
- |
Ø 5 to 32 |
| Rolled pickled |
- |
Ø 5 to 32 |
| Hexagonal |
Rolled pickled |
- |
Hex 12.4 to 28 |
| Billet |
Square |
As rolled or as-heat-treated |
- |
50 to 120 |
Count on us as your trusted partner for all your steel needs, from sourcing to delivery.
-- Our promise
Similar or equivalent steel materials