UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod introduction
Mechanical properties in bars (YS & UTS) are:
Better than those of 316L and also those of 316LN,
Better Corrosion Resistance than that of 316L
The chemical composition is balanced to obtain 40-60% ferrite after annealing between 950 and 1050°C fol-lowed by a fast cooling. The sensitivity to precipitation of intermetallic phases (which cause embrittlement) is much lower than that of Duplex 4462. Typically, sigma phase precipitation requires over 10 hours at 800°C, a situation seldom encountered in processing operations. Precipitation of alfa' phase can occur under long term holding in the 350°C - 550°C temperature range, leading to embrittlement. Thus, the maximum service temperature should not exceed 300°C.
Equivalent material: EN 1.4362, EN X2CrNiN23-4, UNS S32304, ISO 4362-323-04-I, AFNOR Z3CN23-04 Az, DIN 1.4362, SS 2327, ASTM S32304
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod general
| Property |
Value |
| Density |
Density of 7.8 g/cm³ |
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.000014 1/K |
20 to 300°C |
| Thermal conductivity |
Thermal conductivity of 16.7 W/(m·K) |
- |
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 22.0 - 24.0 % |
- |
| Copper |
Copper of 0.1 - 0.6000000000000001 % |
- |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 0.1 - 0.6000000000000001 % |
- |
| Nickel |
Nickel of 3.5 - 5.5 % |
- |
| Nitrogen |
Nitrogen of 0.05 - 0.2 % |
- |
| Phosphorus |
Phosphorus of 0.035 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.015 |
max. |
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 8.000000000000001e-07 Ω·m |
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod mechanical
| Property |
Value |
| Elastic modulus |
Elastic modulus of 200 GPa |
| Elongation |
Elongation of 40.0 - 50.0 % |
| Reduction of area |
Reduction of area of 70.0 - 80.0 % |
| Tensile strength |
Tensile strength of 630.0 - 780.0 MPa |
UGI 4362 Solution annealed, hot rolled bars, turned bars and wire rod application
| Property |
- |
- |
| Application areas |
| Cold Forming |
| Corrosion properties |
| General machinability |
- |
| Test |
Speed (m/min) |
Feed (mm/rev) |
Speed (m/min) |
Feed (mm/rev) |
| Cross-cutting |
60 |
0.04 / 0.015 |
100 |
0.05 / 0.025 |
| Useful life |
| Test |
Speed (m/min) |
Feed (mm/rev) |
Speed (m/min) |
Feed (mm/rev) |
| Cross-cutting |
140 |
0.05 / 0.015 |
140 |
0.07 / 0.035 |
| Useful life |
We offer top-notch steel without compromising on quality or affordability.
-- Our promise
Similar or equivalent steel materials