UGI® 4062 solution annealed, hot rolled bars and wire rod
UGI® 4062 solution annealed, hot rolled bars and wire rod introduction
UGI® 4062 is an austenitic-ferritic or duplex stainless steel with a minimum content of 22 % chromium and 2 % nickel, specially designed as an economically interesting alternative to the grades of the types 1.4301/1.4307 (AISI 304/304L) and 1.4310 (AISI 302/301).
This grade has high mechanical properties and its corrosion resistance is comparable to that of grades 1.4301/1.4310.
Impact strength data: This grade is partially ferritic and has a ductile-brittle transition temperature which restricts its use in the case of large size bars at low temperature.
After ""solution annealing"" in the temperature range 980 °C – 1,050 °C, with water, oil or air cooling, UGI® 4062 is composed of ferrite and austenite in comparable quantities. As a result, it is partially ferromagnetic (it can be ""magnetised"").
During strong cold deformation (wire drawing, etc.), one part of the austenite is transformed into martensite and UGI® 4062 becomes more magnetic.
It is not advised to use UGI® 4062 above 300 °C in order to keep all its properties (refer to hot working paragraph).
Equivalent material: DIN 1.4062, EN 1.4062, UNS S32202, AFNOR X2CrNiN22-2
UGI® 4062 solution annealed, hot rolled bars and wire rod general
| Property |
Value |
| Density |
Density of 7.8 g/cm³ |
UGI® 4062 solution annealed, hot rolled bars and wire rod thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
- |
Coefficient of thermal expansion of 0.000013 1/K |
20 to 100°C |
| - |
- |
Coefficient of thermal expansion of 0.0000135 1/K |
20 to 200°C |
| - |
- |
Coefficient of thermal expansion of 0.000014 1/K |
20 to 300°C |
| Specific heat capacity |
20 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| - |
100 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
200 °C |
Specific heat capacity of 560 J/(kg·K) |
- |
| - |
300 °C |
Specific heat capacity of 590 J/(kg·K) |
- |
| Thermal conductivity |
20 °C |
Thermal conductivity of 15 W/(m·K) |
- |
| - |
100 °C |
Thermal conductivity of 16 W/(m·K) |
- |
| - |
200 °C |
Thermal conductivity of 17 W/(m·K) |
- |
| - |
300 °C |
Thermal conductivity of 18 W/(m·K) |
- |
UGI® 4062 solution annealed, hot rolled bars and wire rod chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 22.0 - 23.8 % |
- |
| Copper |
Copper of 0.5 |
max. |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 0.45 |
max. |
| Nickel |
Nickel of 2.0 - 2.8 % |
- |
| Nitrogen |
Nitrogen of 0.16 - 0.26 % |
- |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.01 |
max. |
UGI® 4062 solution annealed, hot rolled bars and wire rod electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20 °C |
Electrical resistivity of 0.0000008 Ω·m |
| - |
100 °C |
Electrical resistivity of 0.00000085 Ω·m |
| - |
200 °C |
Electrical resistivity of 0.0000009 Ω·m |
| - |
300 °C |
Electrical resistivity of 0.000001 Ω·m |
UGI® 4062 solution annealed, hot rolled bars and wire rod mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy, V-notch |
-46 °C |
Charpy impact energy, V-notch of 10 J |
min. |
| - |
20 °C |
Charpy impact energy, V-notch of 50 J |
min. |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
- |
| - |
100 °C |
Elastic modulus of 194 GPa |
- |
| - |
200 °C |
Elastic modulus of 186 GPa |
- |
| - |
300 °C |
Elastic modulus of 180 GPa |
- |
| Elongation |
- |
Elongation of 30 % |
min., diameter ≤ 120mm |
| Hardness, Brinell |
- |
Hardness, Brinell of 290.0 |
max., diameter ≤ 120mm |
| Tensile strength |
- |
Tensile strength of 650.0 - 900.0 MPa |
diameter ≤ 120mm |
UGI® 4062 solution annealed, hot rolled bars and wire rod application
| Property |
- |
- |
| Application areas |
| Cold Forming |
| Corrosion properties |
| General machinability |
| Heat Treatment |
| Hot forming |
| Other |
Product |
Finish |
Tolerance |
Dimensions (mm) |
| Bars |
Cold transformed by drawing |
h9 |
5.0-28 |
| Wire rod |
- |
- |
5.5-32 |
| Drawn wire |
- |
- |
0.2-10 |
| Bars |
Cold transformed by machining |
h9 |
20-120 |
Collaborate with us to bring your vision to life using our premium-grade steel materials.