SEW 835 Grade GS-50CrV4 quenched and tempered (+QT)
SEW 835 Grade GS-50CrV4 quenched and tempered (+QT) introduction
For components that are stressed in terms of wear and have high strength and good hardening ability, e.g. crane wheels, rope sheaves.
Equivalent material: DIN 1.8160, DIN G51CrV4, EN 1.8160, DIN 1.8159, DIN 50CrV4, DIN 51CrV4, AFNOR 50CrV4, BS 735A50, BS 50CrV4, UNI 50CrV4, SS 2230, AISI 6150, AISI 6150H, SAE 6150, SAE 6150H, JIS SUP10, JIS SUP10M, EN 50CrV4, EN 51CrV4, EN 1.8159, GOST 50HFA, GOST 50HGFA, GB 50CrV4
SEW 835 Grade GS-50CrV4 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
SEW 835 Grade GS-50CrV4 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.46 - 0.54 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.25 - 0.5 % |
| Sulfur |
Sulfur of 0.035 % |
| Vanadium |
Vanadium of 0.07 - 0.12 % |
SEW 835 Grade GS-50CrV4 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 11 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 736 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 520 MPa |
- |