SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT)
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) introduction
The high temperature alloy steel 30CrMoNiV5-11 is used for larger preshaped components in the quenched and tempered condition in turbine and generator installations, in particular as shafts and discs.
The steel is weldable if the relevant measures required are observed.
Equivalent material: UNI 30CrMoV5-11, DIN 1.6946, EN 30CrMoNiV5-11, EN 1.6946
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 550 °C |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 47.1 W/(m·K) |
| - |
100.0 °C |
Thermal conductivity of 47.1 W/(m·K) |
| - |
200.0 °C |
Thermal conductivity of 45.9 W/(m·K) |
| - |
300.0 °C |
Thermal conductivity of 43.8 W/(m·K) |
| - |
400.0 °C |
Thermal conductivity of 41.3 W/(m·K) |
| - |
500.0 °C |
Thermal conductivity of 38.7 W/(m·K) |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13 mm²/s |
| - |
100.0 °C |
Thermal diffusivity of 12.1 mm²/s |
| - |
200.0 °C |
Thermal diffusivity of 11.1 mm²/s |
| - |
300.0 °C |
Thermal diffusivity of 9.9 mm²/s |
| - |
400.0 °C |
Thermal diffusivity of 8.7 mm²/s |
| - |
500.0 °C |
Thermal diffusivity of 7.4 mm²/s |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.28 - 0.34 % |
| Chromium |
Chromium of 1.1 - 1.4 % |
| Manganese |
Manganese of 0.3 - 0.8 % |
| Molybdenum |
Molybdenum of 1 - 1.2 % |
| Nickel |
Nickel of 0.5 - 0.75 % |
| Phosphorus |
Phosphorus of 0.01 - 0.02 % |
| Silicon |
Silicon of 0.15 - 0.3 % |
| Sulfur |
Sulfur of 0.007 - 0.018 % |
| Vanadium |
Vanadium of 0.25 - 0.35 % |
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.21E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.72E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.44E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.28E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.26E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.39E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
SEW 555 Grade 30CrMoNiV5-11 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area, transverse |
20.0 °C |
Reduction of area, transverse of 40 % |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 700 - 850 MPa |
- |
| Yield strength Rp0.2 |
100.0 °C |
Yield strength Rp0.2 of 525 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 500 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 480 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 465 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 445 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 425 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 400 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 365 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 550 MPa |
- |