SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT)
SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT) introduction
The material G20MnMoNi5-5 is suitable for fusion welding and is considered to have a good weldability, since it has been successfully used with good results in cast - welded constructions, especially in combination with rolling mill and forged products made from quenchhardened high-strength fine-grain structural steels. In addition to high values for the 0.2% proof strength, the material distinguishes itself by relatively high values of the notch impact energy at the same time.
Application:
is applied in the mechanical engineering and the vehicle manufacturing, in the plant engineering and crane construction, in the offshore-technology as well as in the underground mining at climatically determined temperatures.
Equivalent material: DIN 1.6309, EN G20MnMoNi5-5, EN 1.6309
SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Nickel Molybdenum Steel |
SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9E-6 - 1.3E-5 1/K |
Typical for Nickel Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Nickel Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 335 - 481 J/(kg·K) |
Typical for Nickel Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 44 W/(m·K) |
Typical for Nickel Molybdenum Steel |
SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 - 0.23 % |
| Chromium |
Chromium of 0.3 % |
| Manganese |
Manganese of 1.2 - 1.5 % |
| Molybdenum |
Molybdenum of 0.45 - 0.6 % |
| Nickel |
Nickel of 0.5 - 0.8 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
SEW 520 Grade G20MnMoNi5-5 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Molybdenum Steel |
| Elongation |
20.0 °C |
Elongation of 16 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Molybdenum Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 550 - 750 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 400 - 450 MPa |
- |