SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT)
Equivalent material: DIN 1.4313, DIN X4CrNi13-4, AFNOR Z6CN13-04, BS 425C11, AISI 415, AISI S41500, SAE 415, SAE S41500, JIS SUSF6NM, JIS SCS5, JIS SCS6, EN X3CrNiMo13-4, EN GX5CrNi134, EN 1.4313, ASTM CA6NM, ASTM F6NM, UNS J91540, UNS S41500, UNS S42400
SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 12 - 13.5 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.9 - 1.1 % |
| Nickel |
Nickel of 3.5 - 5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.025 % |
SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
SEW 520 Grade G-X5CrNi13-4 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 10 - 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 760 - 1130 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 550 - 920 MPa |
- |
Trust our high-quality steel to forge a brighter and stronger future for your projects.
-- Our promise
Similar or equivalent steel materials
Get a quote