SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q)
SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q) introduction
G-X 3 CrNiMoN 26 6 3, for cast parts, like in the production of pumps, has increased resistance against pitting and crevice corrosion in chloride containing solutions, increased strength, is not qualified for service temperatures over 300 °C.
Equivalent material: DIN 1.4468, DIN GX3CrNiMoN26-6-3, JIS SCS33, EN GX2CrNiMoN25-6-3, EN 1.4468, GOST 03Ch24N6AM3
SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.8 g/cm³ |
SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.45E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| Max service temperature | - | Max service temperature of 300 °C | Typical for Duplex Stainless Steel |
| Max service temperature, long | - | Max service temperature, long of 0 - 300 °C | - |
| Melting point | - | Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 450 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 15 W/(m·K) | - |
SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 24.5 - 26.5 % |
| Manganese | Manganese of 2 % |
| Molybdenum | Molybdenum of 2.5 - 3.5 % |
| Nickel | Nickel of 5.5 - 7 % |
| Nitrogen | Nitrogen of 0.12 - 0.25 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.02 % |
SEW 410 Grade G-X3CrNiMoN26-6-3 quenched (+Q) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 GPa | Typical for Duplex Stainless Steel |
| Elongation | 20.0 °C | Elongation of 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Duplex Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Duplex Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 650 - 850 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 450 MPa | - |
| - | 100.0 °C | Yield strength Rp0.2 of 360 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 300 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 265 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 250 MPa | - |