SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q)
SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q) introduction
G-X 3 CrNiMoCuN 26 6 3, for cast parts, like in the chemical industry and in flue gas desulfurisation, has increased resistance against pitting and crevice corrosion in chloride containing solutions, increased strength, is not qualified for service temperatures over 300 °C.
SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.8 g/cm³ |
SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q) thermal
| Property | Temperature | Value |
|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K |
| - | 200.0 °C | Coefficient of thermal expansion of 1.45E-5 1/K |
| - | 300.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K |
| Max service temperature, long | - | Max service temperature, long of 0 - 280 °C |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 450 J/(kg·K) |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 15 W/(m·K) |
SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 24.5 - 26.5 % |
| Copper | Copper of 0.8 - 1.3 % |
| Manganese | Manganese of 2 % |
| Molybdenum | Molybdenum of 2.5 - 3.5 % |
| Nickel | Nickel of 5.5 - 7 % |
| Nitrogen | Nitrogen of 0.12 - 0.25 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.02 % |
SEW 410 Grade G-X3CrNiMoCuN26-6-3 quenched (+Q) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation | 20.0 °C | Elongation of 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 20.0 °C | Tensile strength of 650 - 850 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 480 MPa | - |
| - | 100.0 °C | Yield strength Rp0.2 of 390 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 330 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 295 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 280 MPa | - |