SEW 410 Grade G-X120CrMo29-2 cast condition
SEW 410 Grade G-X120CrMo29-2 cast condition introduction
G-X 120 CrMo 29 9, for armatures and components with higher demands on wear and corrosion resistance in the paper- and cellulose producing industry, photo industry, dyeing factories. Resistant against chlorid and sulfurous acids, ic-resistant.
Equivalent material: DIN 1.4138, EN 1.4138
SEW 410 Grade G-X120CrMo29-2 cast condition general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.7 g/cm³ |
SEW 410 Grade G-X120CrMo29-2 cast condition thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 9.5E-6 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.1E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K | - |
| Melting point | - | Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 500 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 19 W/(m·K) | - |
SEW 410 Grade G-X120CrMo29-2 cast condition chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.9 - 1.3 % |
| Chromium | Chromium of 27 - 29 % |
| Manganese | Manganese of 1 % |
| Molybdenum | Molybdenum of 2 - 2.5 % |
| Phosphorus | Phosphorus of 0.05 % |
| Silicon | Silicon of 2 % |
| Sulfur | Sulfur of 0.03 % |
SEW 410 Grade G-X120CrMo29-2 cast condition electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 6E-7 - 7.5E-7 Ω·m | Typical for Ferritic Stainless Steel |
SEW 410 Grade G-X120CrMo29-2 cast condition mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 220 GPa | Typical for Ferritic Stainless Steel |
| Hardness, Brinell | 20.0 °C | Hardness, Brinell of 260 - 330 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 880 - 1080 MPa | - |
Our stringent quality control measures ensure consistent and reliable steel products.