SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched introduction
The fully austenitic material GX2CrNiN18-13 (the former G-X 2 CrNiN 18 13) possesses a defined low value of the relative magnetic permeability of 1.01 maximum (for castings with a wall thickness of up to 50 mm). It is applied for construction components which an interference or shielding of a magnetic field must not occur at.
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.8 g/cm³ |
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched thermal
| Property | Temperature | Value |
|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.65E-5 1/K |
| - | 200.0 °C | Coefficient of thermal expansion of 1.75E-5 1/K |
| - | 300.0 °C | Coefficient of thermal expansion of 1.75E-5 1/K |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 15 W/(m·K) |
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 16.5 - 18.5 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 12 - 14 % |
| Nitrogen | Nitrogen of 0.1 - 0.2 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.02 % |
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.3E-7 Ω·m |
SEW 395 Grade GX2CrNiN18-13 solution heat-treated and quenched mechanical
| Property | Temperature | Value |
|---|---|---|
| Elongation | 20.0 °C | Elongation of 30 % |
| Tensile strength | 20.0 °C | Tensile strength of 440 - 640 MPa |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 210 MPa |