SEW 090-1 Grade S890Q quenched in a liquid medium and tempered
SEW 090-1 Grade S890Q quenched in a liquid medium and tempered introduction
S890Q is a fluid-tempered high strength weldable fine grained steel with a min. yield point of 890 N/mm². It is applicated for high loaded steel constructions, vehicles, lifting, mining equipment. The usual thickness range amounts 3 to 100 mm. The lowest application temperature accounts for -20°C. The steel is processed by cold forming, at temperatures below the highest permissible stress relieving temperature of 530 to 580 °C. After hot forming at 700 to 1050°C has to be coducted a retempering in order to achieve delivery condition qualities. The steel is combustible and electric arc cuttable subject to appropriate mode of operation. Flame cutting is affected by the surface condition. For product thicknesses above 30 mm is advisable a preheating to 100 to 200 °C in order to assure cold crack resistance. Preheating to 100 to 200 °C is advisable for workpiece temperatures below 5 °C and if the thermal cut edges should be cold formed on processing.
Instructions:
The steel is suitability tested for the construction of pressure vessels and pressure pipes according to the regulations valid in Germany (VdTÜV-material data sheet 417).
Equivalent material: DIN 1.8940, EN S890Q, EN 1.8940
SEW 090-1 Grade S890Q quenched in a liquid medium and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
SEW 090-1 Grade S890Q quenched in a liquid medium and tempered thermal
| Property |
Value |
| Max service temperature, long |
Max service temperature, long of -20 - 0 °C |
SEW 090-1 Grade S890Q quenched in a liquid medium and tempered chemical
| Property |
Value |
| Boron |
Boron of 5E-3 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.8 % |
| Manganese |
Manganese of 1.6 % |
| Molybdenum |
Molybdenum of 0.7 % |
| Nickel |
Nickel of 2 % |
| Niobium |
Niobium of 0.05 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.02 % |
| Vanadium |
Vanadium of 0.1 % |
SEW 090-1 Grade S890Q quenched in a liquid medium and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 11 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 940 - 1100 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 870 - 890 MPa |
- |
Trust our skilled artisans to deliver precision-crafted steel products with impeccable finishes, adding a touch of sophistication to your projects.
-- Our promise