Sandvik 5R75

Sandvik 5R75

Sandvik 5R75 introduction

Sandvik 5R75 is an austenitic, titanium-stabilized stainless chromium–nickel–molybdenum steel.



More technical information and charts that are relevant to the materials corrosion, mechanical and physical performance are displayed in the figures on the right side of the material page.

Datasheet URL:
Sandvik 5R75

Datasheet updated 2019-08-28 09:49 (supersedes all previous editions)

Equivalent material: UNS S31635, ASTM TP316Ti, EN 1.4571, DIN 1.4919, EN X6CrNiMoTi17-12-2, DIN X6CrNiMoTi17-12-2, SS 2350, AFNOR Z6CNDT17-12

Sandvik 5R75 general

Property Temperature Value Comment
Density 23.0 °C Density of 8 g/cm³ -
Recycled Content - Recycled Content of 82.1 % Average recycled content

Sandvik 5R75 thermal

Property Temperature Value Comment
Coefficient of thermal expansion 100.0 °C Coefficient of thermal expansion of 1.65E-5 1/K for 30°C to the mentioned temperature
- 200.0 °C Coefficient of thermal expansion of 1.7E-5 1/K for 30°C to the mentioned temperature
- 300.0 °C Coefficient of thermal expansion of 1.75E-5 1/K for 30°C to the mentioned temperature
- 400.0 °C Coefficient of thermal expansion of 1.8E-5 1/K for 30°C to the mentioned temperature
- 500.0 °C Coefficient of thermal expansion of 1.85E-5 1/K for 30°C to the mentioned temperature
- 600.0 °C Coefficient of thermal expansion of 1.85E-5 1/K for 30°C to the mentioned temperature
- 700.0 °C Coefficient of thermal expansion of 1.9E-5 1/K for 30°C to the mentioned temperature
Specific heat capacity 20.0 °C Specific heat capacity of 485 J/(kg·K) -
- 100.0 °C Specific heat capacity of 500 J/(kg·K) -
- 200.0 °C Specific heat capacity of 515 J/(kg·K) -
- 300.0 °C Specific heat capacity of 525 J/(kg·K) -
- 400.0 °C Specific heat capacity of 540 J/(kg·K) -
- 500.0 °C Specific heat capacity of 555 J/(kg·K) -
- 600.0 °C Specific heat capacity of 575 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 14 W/(m·K) -
- 100.0 °C Thermal conductivity of 15 W/(m·K) -
- 200.0 °C Thermal conductivity of 17 W/(m·K) -
- 300.0 °C Thermal conductivity of 18 W/(m·K) -
- 400.0 °C Thermal conductivity of 20 W/(m·K) -
- 500.0 °C Thermal conductivity of 21 W/(m·K) -
- 600.0 °C Thermal conductivity of 23 W/(m·K) -

Sandvik 5R75 chemical

Property Value Comment
Carbon Carbon of 0.05 % max.
Chromium Chromium of 17 % -
Iron -
Manganese Manganese of 1.3 % -
Molybdenum Molybdenum of 2.1 % -
Nickel Nickel of 12 % -
Phosphorus Phosphorus of 0.03 % max.
Silicon Silicon of 0.5 % -
Sulfur Sulfur of 0.03 % max.

Sandvik 5R75 mechanical

Property Temperature Value Comment
Charpy impact energy -196.0 °C Charpy impact energy of 60 J EN 13445-2 (UFPV-2) and EN 10216-5
Elastic modulus 20.0 °C Elastic modulus of 200 GPa -
- 100.0 °C Elastic modulus of 194 GPa -
- 200.0 °C Elastic modulus of 186 GPa -
- 300.0 °C Elastic modulus of 179 GPa -
- 400.0 °C Elastic modulus of 172 GPa -
- 500.0 °C Elastic modulus of 165 GPa -
Elongation 23.0 °C Elongation of 35 % min., NFA 49-117 with min 45% can be fulfilled.
Hardness, Vickers 23.0 °C Hardness, Vickers of 155 [-] -
Tensile strength 23.0 °C Tensile strength of 510 - 710 MPa -
Yield strength Rp0.1 20.0 °C Yield strength Rp0.1 of 250 MPa min.
- 50.0 °C Yield strength Rp0.1 of 234 MPa min.
- 100.0 °C Yield strength Rp0.1 of 218 MPa min.
- 150.0 °C Yield strength Rp0.1 of 206 MPa min.
- 200.0 °C Yield strength Rp0.1 of 196 MPa min.
- 250.0 °C Yield strength Rp0.1 of 186 MPa min.
- 300.0 °C Yield strength Rp0.1 of 180 MPa min.
- 350.0 °C Yield strength Rp0.1 of 175 MPa min.
- 400.0 °C Yield strength Rp0.1 of 171 MPa min.
- 450.0 °C Yield strength Rp0.1 of 167 MPa min.
- 500.0 °C Yield strength Rp0.1 of 164 MPa min.
- 550.0 °C Yield strength Rp0.1 of 157 MPa min.
Yield strength Rp0.2 20.0 °C Yield strength Rp0.2 of 220 MPa min.
- 50.0 °C Yield strength Rp0.2 of 202 MPa min.
- 100.0 °C Yield strength Rp0.2 of 185 MPa min.
- 150.0 °C Yield strength Rp0.2 of 177 MPa min.
- 200.0 °C Yield strength Rp0.2 of 167 MPa min.
- 250.0 °C Yield strength Rp0.2 of 157 MPa min.
- 300.0 °C Yield strength Rp0.2 of 145 MPa min.
- 350.0 °C Yield strength Rp0.2 of 140 MPa min.
- 400.0 °C Yield strength Rp0.2 of 136 MPa min.
- 450.0 °C Yield strength Rp0.2 of 132 MPa min.
- 500.0 °C Yield strength Rp0.2 of 129 MPa min.
- 550.0 °C Yield strength Rp0.2 of 127 MPa min.