SAE J775 Grade EV-9
Equivalent material: AISI EV-9, UNS S63009
SAE J775 Grade EV-9 general
| Property | Temperature | Value |
|---|---|---|
| Density | 23.0 °C | Density of 8.02 g/cm³ |
SAE J775 Grade EV-9 thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 760.0 °C | Coefficient of thermal expansion of 1.93E-5 1/K | The mentioned value is between 20°C and the mentioned temperature |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
SAE J775 Grade EV-9 chemical
| Property | Value | Comment |
|---|---|---|
| Carbon | Carbon of 0.35 - 0.5 % | - |
| Chromium | Chromium of 12 - 15 % | - |
| Iron | Iron of 64.2 - 73.65 % | Balance |
| Manganese | Manganese of 1 % | - |
| Molybdenum | Molybdenum of 0.2 - 0.5 % | - |
| Nickel | Nickel of 12 - 15 % | - |
| Phosphorus | Phosphorus of 0.05 % | - |
| Silicon | Silicon of 0.3 - 0.8 % | - |
| Sulfur | Sulfur of 0.03 % | - |
| Tungsten | Tungsten of 1.5 - 3 % | - |
SAE J775 Grade EV-9 electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
SAE J775 Grade EV-9 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Reduction of area | 20.0 °C | Reduction of area of 51 % | - |
| - | 650.0 °C | Reduction of area of 41 % | - |
| - | 760.0 °C | Reduction of area of 50 % | - |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 880 MPa | - |
| - | 650.0 °C | Tensile strength of 52 MPa | - |
| - | 760.0 °C | Tensile strength of 320 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 470 MPa | - |
| - | 650.0 °C | Yield strength of 230 MPa | - |
| - | 760.0 °C | Yield strength of 170 MPa | - |