SAE J775 Grade EV-16 For Mechanical Tests: ST+P
Equivalent material: DIN 1.4866, DIN X33CrNiMnN23-8, AFNOR X33CrNiMnN23-8, BS X33CrNiMnN23-8, AISI EV-16, EN X33CrNiMnN23-8, EN 1.4866, ISO X33CrNiMnN23-8, GOST X33CrNiMnN23-8, GB/T 33Cr23Ni8Mn3N, UNS S63018
SAE J775 Grade EV-16 For Mechanical Tests: ST+P general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
SAE J775 Grade EV-16 For Mechanical Tests: ST+P thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.73E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.74E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14.5 W/(m·K) |
- |
SAE J775 Grade EV-16 For Mechanical Tests: ST+P chemical
| Property |
Value |
| Carbon |
Carbon of 0.28 - 0.38 % |
| Chromium |
Chromium of 22 - 24 % |
| Iron |
Iron of 64.59 - 100 % |
| Manganese |
Manganese of 1.5 - 3.5 % |
| Molybdenum |
Molybdenum of 0.5 % |
| Nickel |
Nickel of 7 - 9 % |
| Nitrogen |
Nitrogen of 0.25 - 0.35 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.5 - 1 % |
| Sulfur |
Sulfur of 0.03 % |
| Tungsten |
Tungsten of 0.5 % |
SAE J775 Grade EV-16 For Mechanical Tests: ST+P electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
SAE J775 Grade EV-16 For Mechanical Tests: ST+P mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 205 GPa |
- |
| Elongation A5 |
23.0 °C |
Elongation A5 of 20 % |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 25 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 - 33 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 850 - 1100 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 550 - 634 MPa |
- |