SAE J438b Grade W210 Annealing
Equivalent material: DIN 1.2833, DIN 100V1, AISI W210, JIS SK43, EN 1.2833, DIN 1.2834, DIN 105V, AFNOR 105V, BS 105V, BS BW2, EN 105V, EN 1.2834, ISO 105V, UNS T72302
SAE J438b Grade W210 Annealing general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.72 - 8 g/cm³ |
Typical for Tool And Machining Steel |
SAE J438b Grade W210 Annealing thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Tool And Machining Steel |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 460 J/(kg·K) |
Typical for Tool And Machining Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 17 - 42 W/(m·K) |
Typical for Tool And Machining Steel |
SAE J438b Grade W210 Annealing chemical
| Property |
Value |
| Carbon |
Carbon of 0.95 - 1.1 % |
| Chromium |
Chromium of 0.2 % |
| Manganese |
Manganese of 0.35 % |
| Silicon |
Silicon of 0.35 % |
| Vanadium |
Vanadium of 0.15 - 0.35 % |
SAE J438b Grade W210 Annealing mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 203 - 211 GPa |
Typical for Tool And Machining Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Tool And Machining Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |