SAE J435 Grade 0050B quenched, tempered
SAE J435 Grade 0050B quenched, tempered introduction
Medium Strength Grade
Equivalent material: AISI 0050B, SAE 0050B, UNS J04501
SAE J435 Grade 0050B quenched, tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Medium Carbon Steel |
SAE J435 Grade 0050B quenched, tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for Medium Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
SAE J435 Grade 0050B quenched, tempered chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.4 - 0.5 % |
- |
| Iron |
Iron of 97.69 - 99.1 % |
balance |
| Manganese |
Manganese of 0.5 - 0.9 % |
- |
| Phosphorus |
Phosphorus of 0.04 % |
- |
| Silicon |
Silicon of 0.8 % |
- |
| Sulfur |
Sulfur of 0.045 % |
- |
SAE J435 Grade 0050B quenched, tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J435 Grade 0050B quenched, tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Medium Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 10 % |
- |
| Hardness, HBW |
20.0 °C |
Hardness, HBW of 207 - 225 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 690 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 485 MPa |
- |