SAE J403 Grade 1522
Equivalent material: DIN 1.1133, DIN 20Mn5, AFNOR 20M5, AFNOR 20Mn5, BS 20Mn5, AISI 1522H, AISI 1522, SAE 1522H, JIS SMnC420, JIS STKM19A, JIS 19A, EN 20Mn5, EN 1.1133, GB 20MnG, GB U42203, GB/T 20MnG, GB/T U42203, ASTM 1522, UNS H15220, UNS G15220
SAE J403 Grade 1522 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
SAE J403 Grade 1522 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
SAE J403 Grade 1522 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.18 - 0.24 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 1.1 - 1.4 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.05 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1522 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
SAE J403 Grade 1522 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1522 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |