SAE HNV-3
Equivalent material: AISI HNV-3, SAE HNV-3
SAE HNV-3 general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
SAE HNV-3 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.09E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.13E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
1000.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
1300.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 - 500 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
SAE HNV-3 chemical
| Property |
Value |
| Carbon |
Carbon of 0.4 - 0.5 % |
| Chromium |
Chromium of 8 - 10 % |
| Iron |
Balance |
| Manganese |
Manganese of 0.8 % |
| Nickel |
Nickel of 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 2.7 - 3.3 % |
| Sulfur |
Sulfur of 0.03 % |
SAE HNV-3 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
SAE HNV-3 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 194 - 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
20.0 °C |
Elongation A5 of 14 - 22 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 266 - 325 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 40 - 50 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 1100 - 1350 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 750 MPa |
- |