JIS G4805 Grade X82WMoCrV6-5-4 annealed to achieve spheroidized carbides
Equivalent material: DIN 1.3553, DIN X82WMoCrV6-5-4, AFNOR Z85WCDV6, UNI X82WMoV65, AISI CM2, SAE CM2, EN X80WMoCrV654, EN 1.3553, ISO X82WMoCrV6-5-4
JIS G4805 Grade X82WMoCrV6-5-4 annealed to achieve spheroidized carbides general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.72 - 8 g/cm³ |
Typical for Tool And Machining Steel |
JIS G4805 Grade X82WMoCrV6-5-4 annealed to achieve spheroidized carbides thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Tool And Machining Steel |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 460 J/(kg·K) |
Typical for Tool And Machining Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 17 - 42 W/(m·K) |
Typical for Tool And Machining Steel |
JIS G4805 Grade X82WMoCrV6-5-4 annealed to achieve spheroidized carbides mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 203 - 211 GPa |
Typical for Tool And Machining Steel |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 248 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Tool And Machining Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |