JIS G4317 Grade SUS316L
Equivalent material: ASTM TP316L, ASTM 316L, UNS S31603, ASTM S31603, ASTM F316L, ASTM MT316L, DIN 1.4404, DIN X2CrNiMo18-10, DIN X2CrNiMo17-12-2, DIN G-X2CrNiMoN18-14, DIN GX2CrNiMoN18-14, DIN X2CrNiMoN17-12-2, DIN X2CrNiMo17-13-2, DIN G-X2CrNiMoN18-10, AFNOR Z2CND17-12, BS 316S12, UNI X2CrNiMo1712, SS 2343, SS 2348, SS 2553, AISI 316L, SAE 316L, JIS SCS16, EN X2CrNiMo17-12-2, EN 1.4404, GOST 03Ch17N13M2, GB 022Cr17Ni12Mo2, IS X02Cr17Ni12Mo2, DIN 1.4432, AFNOR Z3CND17-12-03, BS 316S13, JIS SUS316LFB, JIS SUSF316L, EN X2CrNiMo17-12-3, EN 1.4432, GOST 06Ch17N13M3-WD, DIN 1.4435, DIN X2CrNiMo18-14-3, AFNOR Z3CND18-14-03, BS 316S11, BS 316S31, SS 2353, UNE X2CrNiMo18-14-3, AISI 316LMo, SAE 316LMo, JIS SUS316LTBS, JIS SUS316LTP, JIS SUS316LTPY, JIS SUS316LTB, JIS SUSY316L, JIS SUS316J1L, JIS SUSY316J1L, EN X2CrNiMo18-14-3, EN 1.4435, GOST 03Ch17N14M3, GB 00Cr18Ni15Mo3
JIS G4317 Grade SUS316L general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS316L thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS316L electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS316L mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |