JIS G4311 Grade SUH35 ageing treatment after solution treatment
Equivalent material: GB/T 5Cr21Mn9Ni4N, GOST 55Х20Г9АН4, DIN X53CrMnNiN219, NF Z52CMN21-09, BS 349S52, BS 349S54, UNI X53CrMnNiN219, EN X53CrMnNiN21-9, UNE X53CrMnNiN21-09, JIS SUH36, AISI 21-4N, SAE EV-8, DIN 1.4871, DIN X53CrMnNiN21-9, AFNOR Z52CMN21-09, AISI EV-8, EN 1.4871, GB 5Cr2Mn9Ni4N, UNS S63008
JIS G4311 Grade SUH35 ageing treatment after solution treatment general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH35 ageing treatment after solution treatment thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH35 ageing treatment after solution treatment electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH35 ageing treatment after solution treatment mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 8 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 302 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 880 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 560 MPa |
- |
Partner with us to build a solid foundation for success, backed by our expertise in supplying high-quality steel materials.