JIS G4311 Grade SUH31 solution treated
Equivalent material: DIN X45CrNiW189, NF Z35CNWS14-14, UNI X45CrNiW189, UNE X45CrNiSiW18-09, UNE F.320.C, DIN 1.4867, EN 1.4867
JIS G4311 Grade SUH31 solution treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.9 - 8.2 g/cm³ | Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH31 solution treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K | Typical for Austenitic Stainless Steel |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH31 solution treated electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH31 solution treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
| Elongation A5 | 23.0 °C | Elongation A5 of 25 - 30 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 248 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Reduction of area | 23.0 °C | Reduction of area of 35 - 40 % | - |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 690 - 740 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 315 MPa | - |