JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered
Equivalent material: DIN 1.4001, DIN G-X7Cr13, UNE F.8401, JIS SUS4105, EN 1.4001
JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 20.0 °C | Density of 7.6 - 7.7 g/cm³ | Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 20.0 °C | Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K | Typical for Martensitic Stainless Steel |
| Melting point | - | Melting point of 1375 - 1450 °C | Typical for Martensitic Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.08 % |
| Chromium | Chromium of 11.5 - 13.5 % |
| Iron | Iron of 83.75 - 88.5 % |
| Manganese | Manganese of 1 % |
| Nickel | Nickel of 0.6 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |
JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS4105 cold-rolled, annealed, quenched and tempered mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 20.0 °C | Elastic modulus of 220 GPa | Typical for Martensitic Stainless Steel |
| Elongation | 20.0 °C | Elongation of 20 % | - |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 412 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 206 MPa | - |